SWANCOR 1300

Accelerator For UP Resin Curing

A special accelerator  use  to  cure  unsaturated  polyester.  Has  a very  good  characteristic  in  low  temperature  or  high  humidity curing and with excellent strength after cured.

ADVANTAGES

Cost Saving - Dosage is only 1/2-2/3 of normal Cobalt Salt but maintain the same  curing  time  and  provide  additional  strength after cured.

Applicable to low temperature SWANCOR  1300  will  give  short curing time in low temperature without affect the hardness build up of Barcol.

Increase physical properties of FRP.

Example: at 25°C, with 1% of MEKPO in ISO polyester.

Cobalt Salt dosage %

0.2

0.4

0.6

Curing Characteristic

GT

CT

PT

GT

CT

PT

GT

CT

PT

SWANCOR 1300

48.5

70.3

145

15.1

27.1

165

7.5

16.4

167

Normal 6% Cobalt Salt

58.3

82.0

130

27.8

45.4

150

26.4

43.2

156

GT=Gel time (minute)

CT=Curing time (minute)  

PT=Peak temperature (°C)