SWANCOR 901-200 TDS
SWANCOR 901-200  tds pdf

SWANCOR 901-200

Epoxy Vinyl Ester Resin

Product Description

SWANCOR 901-200 is a low viscosity Bisphenol A type epoxy vinyl ester resin. It provides excellent corrosion resistance to a broad range of organic and inorganic acids, alkalis, oxidizing chemicals and salt solution etc. It also provides very good mechanical strength such as tensile and flexural while incorporated with reinforcement such glass fiber, carbon fiber or kevlar fiber etc. The ease of use of SWANCOR 901-200 makes it suitable for various fabrication process, such as pultrusion, RTM, filament winding and vacuum infusion etc. It has good heat resistance distortion temperature as good as SWANCOR 901.

Applications:

  • Chemical storage tanks, pipes.
  • Corrosion resistant flooring while incorporated with aggregates.

Typical properties of liquid resin

Property*1

Value

Appearance

Clear yellow liquid

Solid Content(%)

55±1

Viscosity*2

200±100cps

200±100mPa.s

Gel time*3

15~25mins

Shelf life (months@25ºC)

6

*1 Measurement was obtained under 25оC.

*2 LVT-#3~60rpm@25ºC

*3 6%Cobalt: 0.4phr, 100%DMA: 0.05phr, 55%MEKP: 1.2phr@25ºC

Typical properties of 3.2mm clear casting cured resin

Property

SI*4

 US Standard

Test method

Tensile Strength

80~95MPa

11000~14000 psi

ASTM D638

Tensile Modulus

3.3~3.6GPa

4.0~5.0 X105 psi

ASTM D638

Volume shrinkage

5~6 %

5~6 %

ASTM D2566

Flexural Strength

118~138MPa

17000~20000 psi

ASTM D790

Flexural Modulus

3.1~3.4GPa

4.5~5.4 X 105 psi

ASTM D790

Heat Distortion

Temperature*4

102~105ºC

215~221ºF

ASTM D648

Barcol Hardness

30~38

30~38

ASTM D2583

*4 SI values based on conversion.

*5 Cure condition for HDT: 24 hours at room temperature then 2 hours at 105oC

Typical gel time of SWANCOR 901-200 MEKP system*6

Gel Time

Materials

10-20min

20-40min

40-60min

Temperature

18оС

MEKP

1.80%

1.50%

1.20%

CoOct

0.40%

0.40%

0.40%

DMA

0.10%

0.05%

0.03%

25оС

MEKP

1.50%

1.20%

1.20%

CoOct

0.40%

0.40%

0.30%

DMA

0.06%

0.03%

0.02%

30оС

MEKP

1.20%

1.20%

1.00%

CoOct

0.40%

0.30%

0.30%

DMA

0.05%

0.03%

0.02%

*6 Concentration: Andonox LCR, CoOct: 6%, DMA: 100%

NOTICE IN USE

1. The gel time of SWANCOR 901-200 is affected primarily by catalyst concentration and temperature. The variations of cure characteristics may be caused by variations of catalyst, humidity, pigment, fillers and other additives. It is recommended that the fabricators check the cure characteristics with a small quantity resin before proceeding for bulk production.

2. SWANCOR 901-200 contains organic solvent (styrene). Keep away from heat, sparks and flames.

3. SWANCOR 901-200 is a potentially reactive chemical. Please store it in dark and keep away from direct sunshine.

4. Container, not completely emptied must be closed immediately after use.

5. For material with long storage time, it is recommended to either pump air into the resin or open the cap of containers to prevent gelation.

6. SWANCOR 901-200 is only suitable for hand lay-up, pultrusion and filament winding fabrication process. Others like promoted vinyl resin SWANCOR 901-200-P or pre-thixotroped vinyl resin 901-200-T. can also be provide by customers requested.

MATERIAL SAFETY AND HANDLING INFORMATION

SKIN CONTACT:

Thoroughly wash exposed area with soap and water immediately. Remove contaminated clothing. Launder contaminated clothing before re-use.

EYE CONTACT:

Flush with large amount of water immediately and continuously for 20 minutes, lifting upper and lower lids occasionally. Get medical attention.

INGESTION:

Do not induce vomiting. Keep person warm, quiet and get medical attention. Aspiration of material into the lungs can cause chemical pneumonic which can be fatal.

INHALATION:

If affected, remove individual to fresh air. If breathing is difficult, administer oxygen. If breathing has stopped, give artificial respiration. Keep person warm, quiet, and get medical attention.

PERSONAL PROTECTION:

Do not breathe vapors. High concentration of vapor can be hazardous. Keep out of sewers. Eliminate all sources of ignition in vicinity of spill or released vapor to avoid fire or explosion. For large spills, warn public of downwind explosion hazard. Check area with explosion meter before re-entering area. Ground and bond all containers and handling equipment.

RESIN STORAGE

Keep away from ignition sources; flames, pilot lights, electrical sparks, and sparking tools. NO SMOKING. Do not store in direct sunlight. Store separate from oxidizing materials, peroxides, and metal salts. Keep container closed when not in use. To ensure maximum stability and maintain optimum resin properties, resins should be stored in closed containers at temperatures below 25oC (77oF). Copper or copper containing alloys should be avoided as containers.

SPILLS

Eliminate all ignition sources (flares, flames, including pilot lights electrical sparks). Persons not wearing protective equipment should be exclude from area of spill until clean-up has been completed. Stop spill at source, dike area of spill to prevent spreading, pump liquid to salvage tank. Remaining liquid may be taken up on sand, clay, earth, floor absorbent or other absorbent material and shoveled into containers.

WASTE DISPOSAL

Destroy by liquid incineration in accordance with applicable regulation. Contaminated absorbent should be disposed in accordance to government regulations.

PACKAGE

1. 200kg steel drum