SWANCOR 905-N

EPOXY VINYL ESTER RESIN       

Product Description

SWANCOR 905-N is a high performance brominated epoxy vinyl ester resin. The advantages combines excellent corrosion resistance, good mechanical strength and flame retardancy. SWANCOR 905-N presents excellent performance at elevated temperature and meanwhile excellent flame retardancy. It is designed to provide superior toughness with excellent fatigue resistance due to high heat distortion temperature.

Applications

•  Chemical storage tanks, pipes, flue gas desulfurization systems (FGD), scrubbers, ducts and grating.

•  Corrosion resistant flooring while incorporated with aggregates.

•  Equipment specified to handle mixture of air, exhaust gases or potentially flammable liquids.

•  Military applications such as Kevlar fiber based panels.

Fabrication Methods

•  Can be easily applied by hand lay-up laminating, spray-up, pultrusion, resin transfer molding (RTM) and filament winding.

•  Can be used in polymer concrete casting.

•  Can comply with US FDA regulation CFR 177.2420 if the resin is properly formulated and cured.

Typical properties of liquid resin

Property*1

Value

Appearance

Clear amber liquid

Solid Content (%)

62 +/- 1.5

Viscosity*2

350 +/- 100 cps

350 +/- 100 mPa.s

Specific Gravity

1.15 +/- 0.01

Gel Time (min)*3

15~25

Shelf Life (months)

4

*1  Measurement was obtained under 25оС

*2  LVT-#3-60rpm@25оС

*3  6%Cobalt: 0.4phr, 100% DMA: 0.05phr, 55%MEKP: 1.2phr.

Typical clear casting properties of cured resin

Property

SI*4

US Standard

Test Method

Tensile Strength

80~83MPa

11,000~12,000psi

ASTM D638

Tensile Modulus

3.5~3.7GPa

5.0~5.3 X10*5 psi

ASTM D638

Tensile Elongation

5.2~5.7%

5.2~5.7% ASTM

ASTM D638

Flexural Strength

125~138MPa

18,000~20,000psi

ASTM D790

Flexural Modulus

3.6~3.9GPa

5.2~5.6 X105psi

ASTM D790

Volume Shrinkage

8.0~9.0

8.0~9.0%

ASTM D2566

Heat Distortion Temperature *5

130~136оС

266~277оF

ASTM D648

Barcol Hardness

42 +/-3

42 +/-3

ASTM D2583

 *4  SI values based on conversIon.

*5 Cure condition for HDT: 24 hours at room temperature then 2 hours at 150оС.

Heat resistance of SWANCOR 905-N laminates*6*7

Property

NBS 15-69 Spec.

Testing

Temperature (оС)

SWANCOR 905-N

Laminate

Measurement

Tensile Strength (psi)

12,000

25

65

95

110

120

150

21,500

22,000

21,500

20,000

16,000

14,000

Tensile Modulus

(х105 psi)

-

25

65

95

110

120

150

14,0

14,9

15,3

14,4

13,5

8,1

Flexural Strength (psi)

19,000

25

65

95

110

120

150

25,500

26,000

25,000

23,500

18,000

12,500

Flexural Modulus

(х105psi)

8,0

25

65

95

110

120

150

11,8

11,2

10,5

9,4

9,2

5,6

*6 Construction according to NBS PS 15-69.

*7 Laminate construction is as follows: V/M/M/Wr/M/Wr/M, fiber content: 39~41%, thickness: 6 mm.

Notice in use

1. If SWANCOR 905-N is blended with cobalt-salt promoters, shelf life will be shortened. Promoted SWANCOR 905-N must be used within one week.

2.  The gel time of SWANCOR 905-N is affected primarily by catalyst concentration and temperature. The variations of cure characteristics may be caused by the variations of catalyst, humidity, pigment, fillers and other additives. It is recommended that the fabricators check the cure characteristics with a small quantity resin before proceeding for bulk production.

3. SWANCOR 905-N contains organic solvent (styrene). Keep away from heat, sparks and flames.

4. SWANCOR 905-N is a potentially reactive chemical. Please store it in dark and keep away from heat and direct sunshine.

5.  Containers, not completely emptied must be closed immediately after use.

MATERIAL SAFETY AND HANDLING INFORMATION

SKIN CONTACT:

Thoroughly wash exposed area with soap and water immediately. Remove contaminated clothing. Launder contaminated clothing before re-use.

EYE CONTACT:

Flush with large amount of water immediately and continuously for 20 minutes, lifting upper and lower lids occasionally. Get medical attention.

INGESTION:

Do not induce vomiting. Keep person warm, quiet and get medical attention. Aspiration of material into the lungs can cause chemical pneumonitis which can be fatal.

INHALATION:

If affected, remove individual to fresh air. If breathing is difficult, administer oxygen. If breathing has stopped, give artificial respiration. Keep person warm, quiet, and get medical attention.

PERSONAL PROTECTION:

Do not breathe vapors. High concentration of vapor can be hazardous. Keep out of sewers. Eliminate all sources of ignition in vicinity of spill or released vapor to avoid fire or explosion. For large spills, warn public of downwind explosion hazard. Check area with explosion meter before re-entering area. Ground and bond all containers and handling equipment.

RESIN STORAGE

Keep away from ignition sources; flames, pilot lights, electrical sparks, and sparking tools. NO SMOKING. Do not store in direct sunlight. Store separate from oxidizing materials, peroxides, and metal salts. Keep container closed when not in use. To ensure maximum stability and maintain optimum resin properties, resins should be stored in closed containers at temperatures below 25oC (77oF). Copper or copper containing alloys should be avoided as containers.

SPILLS

Eliminate all ignition sources (flares, flames, including pilot lights electrical sparks). Persons not wearing protective equipment should be exclude from area of spill until clean-up has been completed. Stop spill at source, dike area of spill to prevent spreading, pump liquid to salvage tank. Remaining liquid may be taken up on sand, clay, earth, floor absorbent or other absorbent material and shoveled into containers.

WASTE DISPOSAL

Destroy by liquid incineration in accordance with applicable regulation. Contaminated absorbent should be disposed in accordance to government regulations. 

PACKAGE

Standard packing is 200 kg steel drum.